Product Description:
POLYCIMA 80E90F is a horizontal flame retardant thermoplastic elastomer based on SEBS, featuring a phosphorus nitrogen flame retardant system with high flexibility. This product exhibits excellent mechanical and physical properties, electrical performance, and processability, and complies with regulatory requirements such as ROHS, SVHC, 16P, and PAHS.
Product Application:
Suitable for USB data cables, coaxial cables, drag chain cables, SFP high speed transmission wires, and other products. It can pass the FT 2 flame retardant rating test as specified in UL758. Supports multiple extrusion methods including pressure extrusion, semi tube extrusion, and tube extrusion. Some specifications can also be injection molded.
Performance indicators
Property | Test Method | Unit | Typical Value |
Density | ISO 1183 | g/cm³ | 1.15 |
Tensile Strength | IEC 60811-1-1 | MPa | 14 |
Elongation at Break | IEC 60811-1-1 | % | 320 |
Aging Performance | IEC 60811-1-2 | °C×h | 113°C × 168 h |
Tensile Strength Retention | IEC 60811-1-2 | % | ≥75 |
Elongation at Break Retention | IEC 60811-1-2 | % | ≥75 |
Low Temperature Impact Brittleness Temperature | GB/T 5470 | °C | -25 |
Toxicity Index | - | - | 0.91 |
pH Value | IEC 60754-2 | - | 3.7 |
Electrical Conductivity | - | μS/mm | 0.39 |
Dielectric Strength | GB/T 1408 | kV/mm | 25 |
Oxygen Index | ISO 4589-2 | % | 20 |
Packaging/Storage:
25 kg/bag; transport as general chemical product, store in a dry and cool place, avoid direct sunlight.
Shelf life:
1 year.
Note:
The technical specifications and data provided in this document are for reference only and cannot be used as a basis for inspection or guarantee. Users are responsible for conducting experiments with the products purchased from our company to verify their suitability for the intended processes, applications, performance, and standards. Since the application and processing of our products are beyond our control, any related matters shall be solely the responsibility of the user.
Molding Processing Guide
Injection Molding Guide:
· Shrinkage: 0.010–0.020 inch
· Injection Speed: Medium–High
· Injection Pressure: Medium–High
· Back Pressure: Low–Medium
· Holding Pressure: Sufficient to ensure product shaping inside the mold
· Cooling: Sufficient to allow product demolding
· Screw Temperature (°C):
Extrusion Processing Guide:
Parameter | Value |
L/D Ratio | 20:1 - 25:1 |
Compression Ratio | 2.5 - 3.0 |
Breaker Plate and Screen Pack | Required |
Draw Down Ratio | 5-10% |
Cooling | Water bath cooling |
· Screw Temperature (°C):
Processing Main Considerations:
A: It is recommended to dry at 80°C for 2–4 hours.
B: It is recommended to clean the screw or die head with polypropylene or polyethylene before and after processing this material.
C: Scrap material can be reused. It needs to be dried before use. The addition amount generally should not exceed 15%, and the performance is basically unaffected.