Product Description:
POLYCIMA-150XLF is an XLPE cable compound based on an aluminum-magnesium flame retardant system. This product offers excellent mechanical and physical properties, electrical performance, and processing characteristics, and meets the requirements of environmental regulations such as ROHS, SVHC, 16P, and PAHS.
Product Applications:
This product complies with UL758 standards and is suitable for UL150°C rated electronic wires, as well as wires such as UL3398 and UL3321. It passes the single horizontal flame test.
Performance | Test Method | Unit | Typical Value |
Density | ISO 1183 | g/cm³ | 1.36 |
Tensile Strength | IEC60811-1-1 | MPa | 15 |
Elongation at Break | IEC60811-1-1 | % | 380 |
Aging Performance | IEC60811-1-2 | °C × h | 180°C × 168 |
Tensile Strength Retention | IEC60811-1-2 | % | ≥80 |
Elongation at Break Retention | IEC60811-1-2 | % | ≥80 |
Low Temperature Brittleness Temperature | GB/T5470 | °C | -25 |
Toxicity Index |
|
| 1.0 |
pH Value | IEC60754-2 |
| 5.0 |
Electrical Conductivity |
| μs/mm | 0.48 |
Dielectric Strength | GB/T1408 | KV/mm | 25 |
Oxygen Index | ISO4589-2 | % | 24 |
Packaging/Storage:
25 kg/bag. Transport as general chemical product. Store in a dry, cool place away from direct sunlight. Shelf life: 1 year.
Note:
The technical property indicators and data provided in this document are for reference only and cannot be used as a basis for inspection or guarantee. Users who purchase our products are also responsible for conducting their own tests to verify whether the product is suitable for their intended processes, applications, performance requirements, and standards. Since the application and processing of our products are beyond our control, any related issues shall be solely the responsibility of the user.
Extrusion Processing Guide:
Parameter | Value |
L/D Ratio | 20:1 - 25:1 |
Compression Ratio | 1.8 - 2.3 |
Breaker Plate and Screen Pack | Required |
Draw Down Ratio | 5-10% |
Cooling | Water bath cooling |
Screw Temperature (°C):
Processing Precautions:
A: It is recommended to dry the material at 90°C for 2–4 hours.
B: It is recommended to clean the screw or die head with a special purging compound before and after processing this material.